LIQUID RESIN CURED RESIN APPLICATION
Type Appearance Acid value
(Mg KOH/gm)		 Viscosity at 25 C (CPs) Specific Gravity At 25 C Refractive Index At 25 C Volatile Content (%) Gel time at 25 C
(in minutes) temp		 Gel time at 82 C
(min.) /PE (C)		 Barcol Hardness Heat Distortion ± 3 (C)
General Purpose Clear to Pale Yellow Liquid 20±2 700-250 1.10-1.13 1.53-1.55 35±2 15 9-13
165-170		 42-45 70 Medium reactivity premium G.P. Resin, suitable for hand lay-up molding, filament winding etc. Extensively used to manufacture normal FRP products. Widely used for potting of chokes.
General Purpose Clear to Pale Yellow Liquid 20±4 700-250 1.10-1.13 1.53-1.54 33±3 20 9-13
160-170		 35-40 65 General purpose resin of medium reactivity. Its bonding & impact strength is very high. Widely used for polyester Putty.
RTM Clear to Pale Yellow Liquid 22±2 200-300 1.08-1.10 1.53-1.54 38±3 15 10-12
180-200		 42-45 70 GP resin used widely in resin transfer molding application.
Food Grade Clear to Pale Yellow Liquid 18±2 400-100 1.08-1.09 1.52-1.54 39±2 15 10-14
165-170		 40-45 65 GP resin, to manufacture FRP products used in storage and handling of Food articles in FRP based Food Packing/Industries
Roof Lite Clear to Pale Yellow Liquid 22±2 200-50 1.08-1.10 1.52-1.54 41±2 40 16-20
165-170		 40-45 70 UV stabilized medium reactive resin used for marking Translucent Roof lite sheets.
Roof Lite Clear to Pale Yellow Liquid 22±2 200-50 1.10-1.13 1.52-1.54 41±2 40 16-20
170-180		 40-45 70 UV stabilizer medium reactive resin used for marking Translucent Roof lite sheets. It can also be used for decorative laminates.
SMC Clear to Pale Yellow Liquid 19±2 900-1600 1.10-1.13 1.53-1.54 32±2 15 8-12
160-170		 43-48 70 High reactivity resin designed specially foe manufacture of SMC.
DMC Clear to Pale Yellow Liquid 21±2 3000-300 1.11-1.14 1.53-1.54 29±3 15 8-12
160-170		 50-52 70 High reactivity resin designed specially foe manufacture of DMC. It can also effectively be used in press molding. Resin designed for hot press molding for low shrinkage.
Fire Retardant White Liquid 16±2 600-1100 1.15-1.20 NA 30±2 15 10-12
150-170		 40-45 60 Medium reactivity resin has very low inflammability can be safely used to make articles where safety from fire hazards is necessary.
Fire Retardant SMC White Liquid 16±2 1000-1800 1.15-1.20 NA 28±2 15 8-12
150-170		 40-45 60 High reactivity resin designed especially for manufacture of SMC having fire retardant properties.
RTM FR Milky white Liquid 16±2 500-200 1.15-1.20 NA 32±2 15 10-15
145-150		 30-35 60 General purpose resin used widely in resin transfer molding application- very low inflammable resin orthophthalic based.
Fire Retardant White Liquid 16±2 1000-1800 1.20-1.30 NA 30±5 15 10-12
165-170		 48-50 60 Low-cost Fire-Retardant Polyester Resin.
Normal Clear to Pale Yellow Liquid 15±2 500-800 1.10-1.13 1.53-1.54 39±2 15 9-12
170-200		 45-50 100 High reactivity resin used against mild corrosion resistance of acids. It is widely used to make FRP chemicals process plants, storage tank, pipes, exhaust hood etc. imparts good mechanical and electrical properties.
SMC/DM C Clear to Pale Yellow Liquid 14±2 1000-1800 1.10-1.13 1.53-1.54 34±2 15 9-12
185-200		 45-50 100 Highly reactivity high viscous resin specially designed for SMC/DMC application.
Fire Retardant White Liquid 14(max) 600-1100 1.15-1.25 NA 32±2 15 15-20
155-200		 40-45 80 Highly reactive very low flammability fire retardant resin.
Food Grade Clear to Pale Yellow Liquid 14±2 300-200 1.06-1.10 1.52-1.54 40±2 15 15-18
185-200		 40-45 100 Polyester resins used in food processing industry.
PVC Grade Clear to Pale Yellow Liquid 14±2 400-200 1.08-1.10 1.52-1.54 40±2 15 6-8
185-200		 40-45 100 Medium reactive polyester resin for FRP laminations on PVC. It has excellent bonding with PVC.
RTM Clear to Pale Straw Liquid 15±2 250-300 1.09-1.12 1.53-1.54 45±2 15 10-12
180-200		 42-45 100 Isopthalic Resin used widely in resin transfer molding application as per IS- 6746
RTM FR Milky white Liquid 12±2 500-200 1.15-1.20 NA 33±2 15 10-15
155-170		 40-45 80 Very low inflammability Isophthalic based resin widely used in resin transfer molding.
SMC/DMC Clear to Hazy Liquid 12±2 400-700 1.09-1.12 1.53-1.54 38±2 15 9-12
180-190		 40-45 100 Polyester Resin used for SMC/DMC application.
Normal Clear to Hazy Liquid 16±2 400-700 1.09-1.12 1.53-1.54 38±2 15 9-12
180-190		 40-45 100 Terephthalic acid based polyester Resin suitable for use in fiberglass Rain forced plastics molding application where superior water resistance, heat resistance is desired in comparison to general purposes polyester resin
Orthopthalic Opaque Pale Yellow Liquid 19±2 Thixo Tropic 1.10-1.15 NA 34±2 15 9-12
165-170		 NA 70 Thixotropic Gel coat resin to be used for a smooth top surface. This is used as a top coat of FRP articles to make the surface coloured, elastic and highly glossy
Isopthalic Opaque Pale Yellow Liquid 12±2 Thixo Tropic 1.10-1.15 NA 38±2 15 9-12
185-200		 NA 100 Thixotropic Gel coat resin based on Isopthalic Polyester Resin. It has high impact resistance; durability is much higher with very low water absorption.
Orthopthalic Fire Retardant Opaque Pale Yellow Liquid 14±2 Thixo Tropic 1.15-1.20 NA 30±2 15 12-15
165-175		 NA 60 Orthopthalic based Fire retardant Gel Coat. It is used as a top coat on fire retardant articles.
Isopthalic Fire Retardant Opaque Pale Yellow Liquid 10±2 Thixo Tropic 1.15-1.20 NA 32±2 15 12-15
180-200		 NA 80 Isopthalic based Fire retardant Gel coat. It is used as a top coat on fire retardant articles.
Bisphenol Fumarate
Bisphenol Grade Pale Yellow Liquid 12±2 550-100 1.06-1.08 1.53-1.54 49±2 20* 35-40
175-200		 42-48 135 Based on Prepoxylated Bisphenol Structure offers excellent corrosion resistance to acid mild alkalies, salts, solvents. Suitable for moulding, hand lay-up and filament winding applications.
Special
Tooling Grade Clear to hazy liquid 16±2 600-700 1.10-1.13 1.53-1.54 32±2 15 min 5-7
210-220		 55-60 100 Tooling grade resin having good corrosive resistance
Lamination Grade Clear to Pale Yellow liquid 25±3 125-145 1.06-1.09 1.53-1.54 41±1 8 min 9-11
170-190		 40-45 102 Press moulded laminates. It is also suitable with natural fibers.
Vinyl Ester
Normal Grade Pale Yellow to Light 10±2 400-600 1.05-1.06 1.53-1.54 35±5 20* 35-40
120-140		 30-35 100 Chemicals structure intermediate between those of epoxides and polyester, excellent wetting and bonding to glass fibers. Retains high elongation at moderate and high temp. excellent chemicals resistance and low shrinkage
Fire Retardant Brownish white 8±2 400-800 1.15-1.18 NA 30±2 20* 35-40
120-140		 30-35 100 Vinyl Easter Resin based Fire Retardant Resin. It has chemicals resistance towards acids and alkalis and has excellent fire retardant properties.